LNP™ THERMOTUF™ WF006I compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EVkr9a_LNP-THERMOTUF-WF006I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* WF006I is a compound based on PBT containing 30% Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound WF-1006 HI Product reorder name: WF006I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.29 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8960 | MPa | ASTM D638 |
| -- | 6520 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 107 | MPa | ASTM D638 |
| Yield | 109 | MPa | ISO 527-2 |
| Break | 106 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield | 3.2 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Break | 4.0 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7520 | MPa | ASTM D790 |
| -- | 8620 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 174 | MPa | ASTM D790 |
| -- | 181 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 190 | J/m | ASTM D256 |
| 23°C 2 | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 3 | 64 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 17.2 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 210 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-5570U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| APEX® 3200-80NT | Teknor Apex Company | PVC, Flexible | APEX® |
| GAPEX® RPP10EV02NA | Ferro Corporation | PP, Unspecified | GAPEX® |
| Hostaform® C 13021 10/1570 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LUVOCOM® 1-8864/ES | LEHVOSS Group | Nylon 66 | LUVOCOM® |