Rynite® FR530 BK507
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Rynite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EV9ppz_Rynite-FR530-BK507.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Flame Retardant, Polyethylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2 |
| Flexural Modulus | 10500 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 30 | kJ/m² | |
| 23°C | 40 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 243 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| Melting Temperature 1 | 252 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Flow : -40 to 23°C | 2.0E-5 | cm/cm/°C | |
| Transverse | 9.0E-5 | cm/cm/°C | |
| Transverse : -40 to 23°C | 7.3E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 0.400 mm | 155 | °C | |
| 0.750 mm | 155 | °C | |
| 1.50 mm | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.350 mm | V-0 | ||
| 1.50 mm | V-2 5VA |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP242N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Vinylbond 95-950-60 | Colorite Polymers | PVC, Flexible | Vinylbond |
| NEXUS PC/PBT PC/PBT 7820 | Nexus Resin Group, LLC. | PC+PBT | NEXUS PC/PBT |
| Hetron™ FR 992 | Ashland Performance Materials | Vinyl Ester | Hetron™ |
| Interpol 47-5134/47-5205 | Cook Composites and Polymers | Polyester, TS | Interpol |