| PPE+PA Blend with 10% glass fibre; high impact; very high temperature resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 67.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (3.20 mm) | 0.90 - 1.1 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4050 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 96.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 11 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 180 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 80°C) | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 285 - 310 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Maximum Residence Time: 4 to 10 minInjection Pressure: moderate to high |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSHINE PW310G13 | Polyram Ram-On Industries | SAN | RAMSHINE |
| Spartech Polycom WI50D34SR | Spartech Polycom | PVC Alloy | Spartech |
| Braskem PP CP 270R | Braskem | PP Impact Copolymer | Braskem PP |
| Epic Urethane S7344 | Epic Resins | PUR, Unspecified | Epic Urethane |
| Karina BLACK PVC COMPOUND -E 858-48/ 1-CY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |