ISPLEN® PP 020 G3E
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ESgFYm_ISPLEN-PP-020-G3E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ISPLEN® PP 020 G3E is a low melt flow rate polypropylene homopolymer with a reinforced formulation of thermal stabilization suitable for protecting the polymer during extrusion process and final use. His crystalline structure gives a good balance between stiffness and tensile strength resistance. TYPICAL APPLICATIONS
Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.91 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 151 | °C | ISO 306/A |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL B 15 SL 20 TC | RIALTI Srl | PP, Unspecified | RIALFILL |
| Tecomid® NA40 GR13 NL100 MB | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Tempalux® 20% GF | Westlake Plastics Company | PEI | Tempalux® |
| Iupiace® AH80 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LUVOCOM® 1-RG 2 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |