PLANAC BSH-130
| Category: | PBT+PS , Polybutylene Terephthalate + PS |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | PLANAC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ESLqTK_PLANAC-BSH-130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLANAC BSH-130 is a polybutylene terephthalate + PS (PBT + PS) product, which contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in North America or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ASTM D638 |
| Tensile Strength | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 8500 | MPa | ASTM D790 |
| Flexural Strength | 160 | MPa | ASTM D790 |
| Compressive Strength | 130 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 200 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 2.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 28 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 150 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 550 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value shown for Comparative Track Index, UL 746, was tested in accordance with ASTM D3638.Flexural Elongation @ Break, ASTM D790: 2.5% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 230 - 270 | °C | |
| Middle Temperature | 230 - 270 | °C | |
| Front Temperature | 230 - 270 | °C | |
| Mold Temperature | 40.0 - 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baydur® TB 100-30 Thermal Break System | Covestro - PUR | PUR-MDI | Baydur® |
| Carbotex KG-20MRA | Kotec Corporation | PC | Carbotex |
| Flontech® FT-PPS15-CARR10-M2-2 | Guarniflon S.p.A. - Flontech Division | PTFE+PPS | Flontech® |
| LNP™ THERMOCOMP™ JF002R compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |
| Sylvin 8225-80FR Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |