TECHNYL® A 60G1 V25 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ESL855_TECHNYL-A-60G1-V25-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHNYL® A 60G1 V25 Natural is a 25% GF reinforced organophosphorous flame retarded grade based on a patented high flow polyamide 66 resin. This product is heat stabilized and provides optimized injection moulding performance. This product is available in |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (275°C/0.005 kg) | 27 | -- | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.83 | -- | % | ISO 62 |
| Outdoor Suitability | f1 | -- | UL 746C | |
| Molding Shrinkage Isotropy | 0.500 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 8000 | MPa | ISO 527-2/1A |
| Tensile Strength | ||||
| Break | 130 | -- | MPa | ASTM D638 |
| Break | 142 | 88.0 | MPa | ISO 527-2/1A |
| Tensile Elongation | ||||
| Break | 2.8 | -- | % | ASTM D638 |
| Break | 2.0 | 2.7 | % | ISO 527-2/1A |
| Flexural Modulus | 8300 | -- | MPa | ASTM D790 |
| Flexural Strength | 195 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ||||
| -30°C | 60 | -- | kJ/m² | ISO 179/1fU |
| 23°C | 65 | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | 95 | -- | J/m | ASTM D256 |
| 23°C | 6.8 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 246 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/Af |
| Melting Temperature | ||||
| -- | 263 | -- | °C | ISO 11357-3 |
| -- | 262 | -- | °C | ASTM D3418 |
| CLTE - Transverse (23 to 85°C) | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength | 30 | 28 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 550 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| 3.20 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.60 mm | 775 | -- | °C | |
| 3.20 mm | 775 | -- | °C | |
| Oxygen Index | 33 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 275 | °C | |
| Middle Temperature | 275 to 280 | °C | |
| Front Temperature | 280 to 285 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEOFLON™ LP-1030 | Daikin Fluorochemicals (China) Co., Ltd. | Fluoropolymer | NEOFLON™ |
| EXCELLOY CKF51G10 | Techno Polymer Co, Ltd. | PC+ABS | EXCELLOY |
| Hostacom EP KC 10 Z 81 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LEXAN™ PC1000R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Lutene® H ME2500 | LG Chem Ltd. | HDPE | Lutene® H |