EPO-TEK® T905-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EPhGNX_EPO-TEK-T905-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Two component, thermally conductive, electrically insulating epoxy suggested for general adhesive bonding, sealing, potting and encapsulation applications. Replacement for EPO-TEK® T905. Formerly 78-121-1 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 50.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 346 | °C | |
| Die Shear Strength - >15 kg (23°C) | 35.2 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 175 | °C | |
| Intermittent | -55 to 275 | °C | |
| Storage Modulus (23°C) | 3.03 | GPa | |
| Thixotropic Index | 1.60 | ||
| Weight Loss on Heating | |||
| 200°C | 0.27 | % | |
| 250°C | 1.1 | % | |
| 300°C | 2.7 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 40.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.5E-5 | cm/cm/°C | |
| -- 3 | 1.3E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.59 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 20 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Amber | ||
| -- 5 | Grey | ||
| Density | |||
| Part B | 1.03 | g/cm³ | |
| Part A | 2.18 | g/cm³ | |
| Viscosity 6(23°C) | 6.0 to 13 | Pa·s | |
| Curing Time (80°C) | > 1.0 | hr | |
| Pot Life | 30 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 4.83 | ||
| Volume Resistivity (23°C) | > 1.0E+12 | ohms·cm | |
| Dissipation Factor (1 kHz) | 9.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 112329 | RTP Company | Unspecified | RTP |
| Altuglas® HFI-10 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Durethan® BKV 135 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Elastron® V V101.A35.B | Elastron USA, Inc. | TPV | Elastron® V |
| INNOPOL® PP CS 2-9302 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |