Geon™ 210 Series 217 Blending Resin
| Category: | PVC Homopolymer , Polyvinyl Chloride Homopolymer |
| Manufacturer: | Mexichem Specialty Resins, Inc. |
| Trademark: | Geon™ 210 Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EPG1Dy_Geon-210-Series-217-Blending-Resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon® 217 is a low to medium molecular weight homopolymer blending resin intended for use as a formulation tool in plastisol formulations.It improves air release performance resulting in reduced scrap rates. It decreases high shear viscosity providing an improved 'ease of coating' performance resulting in a more uniform plastisol coating and improving line up time. It reduces viscosity aging characteristics, providing increased plastisol usage (pot life). It reduces surface gloss of films or coated products resulting in less surface blocking and improved handling. Geon® 217 is recommended for solid and foamed plastisol applications such as coated fabric, cast films and coatings, foam mats and pads. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| K-Value 1 | 67.0 | ||
| Apparent loose density 2 | 0.530 | g/cm³ | Internal method |
| Intrinsic Viscosity | 0.92 | ASTM D1243-60-A | |
| Particle Size | Internal method | ||
| < 52 Micron 3 | 94.2 | % | Internal method |
| < 74 Micron 4 | 99.0 | % | Internal method |
| Average Particle Size 5 | 30.0 | µm | Internal method |
| Relative Viscosity 6 | 2.23 | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze - Fused 5 mins (177°C) 7 | 54 | % | Internal method |
| Gloss- 60° Fused 5 mins (177°C) 8 | 18 | % | Internal method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brokfield Viscosity | Internal method | ||
| FF 9 | 2.30 | Pa·s | Internal method |
| Initial Viscosity @ 20 rpm 10 | 2.38 | Pa·s | Internal method |
| Initial Viscosity @ 2rpm 11 | 2.30 | Pa·s | Internal method |
| One Day Viscosity @ 20rpm 12 | 2.40 | Pa·s | Internal method |
| Cut off the outflow- 95 psi 13 | 522.00 | g/10 min | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Vinyl Chloride Monomer 14 | ppm | Internal method | |
| Volatiles 15 | 0.050 | % | Internal method |
| polymerization process | Suspension | ||
| Gel temperature- PP 16 | 92 | °C | Internal method |
| Vinyl diffuser 17 | 95.0 | µm | Internal method |
| Note:The value set forth represent "typical" values and Mexichem Specialty Resins, therefore, makes no representation that the material in any particular shipment will conform to the listed properties.Packaging: This resin is shipped in multi-wall paper bags, net weight 50 lbs, 2500 lbs per pallet. Information shown on the package includes commercial identification number, lot and weight.Geon® ALTC (formulation): 60phr Geon® 121A, 40phr Geon® 217, 57phr DINP, 3phr ESO, and 2phr Therm-Chek SP 120 LOHFGeon® STP 1203(formulation): 60phr Geon® 178, 40phr Geon® 217,and 60phr DOP |
| Note Message | |
|---|---|
| 1 . | Interrelationship |
| 2 . | Geon® STP 1169 |
| 3 . | <53 µ |
| 4 . | Geon® DFT 1466 |
| 5 . | Geon® 812 |
| 6 . | 1% Cyclohexanone |
| 7 . | 60, melting for 3 minutes, ALTC-65 |
| 8 . | 60, melt for 5 minutes, ALTC-65 |
| 9 . | Geon® ALTC 22 (with provided formulation) |
| 10 . | One day, V12,Geon®1010 |
| 11 . | Initial, V12,Geon®1010 |
| 12 . | Geon® ALTC 22 (with provided formulation) |
| 13 . | 95 psi |
| 14 . | Geon® STP 1005 |
| 15 . | Bags, Geon®793 |
| 16 . | Geon® ALTC 29 (with provided formulation) |
| 17 . | Geon® STP 1203 (with provided formulation) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synres® PP G30 19 | Teknor Apex Company | PP, Unspecified | Synres® |
| Chiao Fu PBT PBT819G30 NAT | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| Daelim Po1y® PH-630 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| POLYfill PPC TS6020 E20 | Polykemi AB | PP Copolymer | POLYfill |
| MAXATEL® AH100T-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |