Starex HG-0760GP
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EOgHMO_StarexHG0760GP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex HG-0760GP is an acrylonitrile butadiene styrene (ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: electrical appliances. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.35 - 0.43 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.37 - 0.45 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.37 - 0.45 | % | ISO 2577 |
| Traffic : 3.20mm | 0.35 - 0.43 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 108 | ASTM D785 | |
| R scale | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 32.0 | MPa | ASTM D638 |
| Fracture | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 24 | % | ASTM D638 |
| Fracture | 21 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2000 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 59.0 | MPa | ASTM D790 |
| -- 8 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 240 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 230 | J/m | ASTM D256 |
| 23°C 10 | 23 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 88.0 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 98.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 76.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 93.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 96.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 210 - 220 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 160 - 180 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Pressure | 49.0 - 147 | MPa | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roscom PVC 601VO-75/80 | Roscom, Inc. | PVC, Flexible | Roscom PVC |
| NEO-ZEX™ 3510F | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| LEXAN™ BY2710X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Plaslube® POM CO GF25 TL5 | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |
| Polifil® Nylon 628L | The Plastics Group | Nylon 66 | Polifil® Nylon |