Wondel® P PN0T is a Polypropylene material. It is available in Asia Pacific. Important attributes of Wondel® P PN0T are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.4 to 1.7 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Stress | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 108 | °C | ISO 75-2/B |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LSG286G | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Electrafil® HDPE C BK003 | Techmer Engineered Solutions | HDPE | Electrafil® |
| Kingfa API-1109 | Kingfa | PP, Unspecified | Kingfa |
| OmniLon™ PA6/6 U IM20 BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| API II 390 | API II, Inc. | PS (GPPS) | API II |