Ultramid® HPN 9362
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ENu4sk_Ultramid-HPN-9362.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid HPN 9362 is a 40% mineral reinforced, impact modified PA6 injection molding compound. It is one of the High Productivity Nylon series having improved surface appearance while reducing cycle time. It possesses excellent balance of strength, stiffness and toughness combined with a high level of drop weight impact, excellent processability and chemical resistance to greases, oils and hydrocarbons. Applications Ultramid HPN 9362 is generally recommended for applications such as wheel cover and hubs, mirror housings, appliance components, power tool housings, small engine pulleys, and trimmer spools. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.41 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.0 | -- | % | |
| Water Absorption | ||||
| Saturation | 4.9 | -- | % | ASTM D570 |
| Saturation, 23°C | 4.9 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 1.4 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4330 | 2900 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Yield, 23°C | 64.0 | 45.0 | MPa | ASTM D638 |
| Yield, 23°C | 65.0 | 45.0 | MPa | ISO 527-2 |
| Break, 23°C | 62.0 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield, 23°C | 3.0 | 27 | % | ASTM D638, ISO 527-2 |
| Break, 23°C | 15 | 30 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 5230 | -- | MPa | |
| 23°C | 4000 | 1560 | MPa | |
| 65°C | 1250 | 970 | MPa | |
| 90°C | 770 | 850 | MPa | |
| 121°C | 750 | 740 | MPa | |
| Flexural Strength | ASTM D790 | |||
| -40°C | 180 | 155 | MPa | |
| 23°C | 109 | 50.0 | MPa | |
| 65°C | 45.0 | 35.0 | MPa | |
| 90°C | 30.0 | 30.0 | MPa | |
| 121°C | 30.0 | 25.0 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 3.0 | -- | kJ/m² | |
| 23°C | 6.0 | -- | kJ/m² | |
| Notched Izod Impact (23°C) | 86 | -- | J/m | ASTM D256 |
| Drop Impact Resistance (23°C) | 74.6 | -- | J | Internal Method |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | -- | °C | ASTM D648 |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 2.3E-5 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6225R E49 | Spartech Polycom | PP, Unspecified | Spartech |
| KIBIPOL® PR-255 | CHI MEI CORPORATION | IIR | KIBIPOL® |
| ESTOPLAST EP 2030BB12 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| ISOTHANE® 3075A-FR | Great Eastern Resins Industrial Co., Ltd. (GRECO) | TPU-Polyether | ISOTHANE® |
| Sumikon® PM-TX250 | SBHPP | Phenolic | Sumikon® |