DOW™ LDPE 7010E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ENeVNI_DOW-LDPE-7010E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDPE 7010E is a High Speed Extrusion Coating Resin Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 11.4 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 540 | % | ISO 527-2 |
| Flexural Modulus | 209 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission Rate 1 | 0.67 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 108 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 260 to 320 | °C | |
| Draw Down - From 15 g/m² at 100 m/min 2(320°C) | 480 | m/min | Internal Method |
| Minimum Coating Weight - Calculated 3 | 6.0 | g/m² | Internal Method |
| Neck-in - 25 g/m² at 100 m/min 4(320°C) | 152.0 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 1.0 mil (25µm) coating onto 50 lb Kraft paper. |
| 2 . | 25 g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 3 . | 25 g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| 4 . | 25 g/m² coating onto paper substrate and/or coating web at 250 mm air gap and -15 nip off-set. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPP5A30CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| SABIC® PPcompound 15T1020 | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PPcompound |
| BIOH™ Polyol X-0210 | Cargill Industrial Bio-Products | Biodeg Polymers | BIOH™ Polyol |
| BESTNYL SI00VI02BX | Triesa Plastics | Nylon 6 | BESTNYL |
| BP RPP 3009 GKW | Buckeye Polymers, Inc. | PP, Unspecified | BP |