Infino NH-1029
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ENNohT_InfinoNH1029.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Infino NH-1029 is a polycarbonate acrylonitrile butadiene styrene (PC ABS) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 110 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 59.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2400 | MPa | ASTM D790 |
| Flexural Strength 3 | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 390 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.2 mm | V-1 | UL 94 | |
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80 | °C | |
| Hot air dryer | 80 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Hot air dryer | 2.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 180 - 220 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Injection Pressure | 98.0 | MPa | |
| Back Pressure | 1.00 | MPa | |
| Screw Speed | 30 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 240°CHot Runner Valve Nozzle Temperature: 240°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E 398 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| CALP 1100G-1 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| EPLAMID 66 GX2 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| IROGRAN® A 85 E 4607 E | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LNP™ LUBRICOMP™ KN001 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |