Ferro PP TPP20AE37UL-WH
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ENFggk_Ferro-PP-TPP20AE37UL-WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP TPP20AE37UL-WH is a Polypropylene material filled with 20% talc. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Ferro PP TPP20AE37UL-WH are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 34.5 | MPa | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 50.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 204 to 210 | °C | |
| Middle Temperature | 210 to 213 | °C | |
| Front Temperature | 213 to 216 | °C | |
| Nozzle Temperature | 216 to 218 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.138 to 0.345 | MPa | |
| Screw Speed | 100 to 150 | rpm | |
| Clamp Tonnage | 2.8 to 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL B 15 SL 20 TC | RIALTI Srl | PP, Unspecified | RIALFILL |
| GAPEX® RPP10EU56BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Elastane™ 4720-80A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Haysite Plastics H722 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Exceed™ 3812CB | ExxonMobil Chemical | mPE | Exceed™ |