Reny® 1071
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EMD32w_Reny-1071.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 1071 is a Polyarylamide (PARA) material filled with 55% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1071: Flame Rated. Typical application of Reny® 1071: Engineering/Industrial Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.70 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.21 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.10 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 24900 | 23700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 264 | 237 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.6 | 1.6 | % | ISO 527-2 |
| Flexural Modulus | 20600 | 20900 | MPa | ISO 178 |
| Flexural Stress | 423 | 384 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 17 | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 83 | 66 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 230 | -- | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-5 | -- | cm/cm/°C | |
| Transverse | 3.0E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers HDPE 50 0149 | Network Polymers, Inc. | EHMWPE | Network Polymers HDPE |
| Fainplast PVC RKS 325 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| EcoBlend® HML5150 | Shanghai KumhoSunny Plastics Co., Ltd. | PLA+PMMA | EcoBlend® |
| Karina IVORY PVC COMPOUND 600D35/1-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8773-60D Grey 9504 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |