LNP™ LUBRICOMP™ GL003 compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EM6DlQ_LNP-LUBRICOMP-GL003-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* GL003 is a compound based on Polysulfone resin containing 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound GL-4030 Product reorder name: GL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.83 | % | ISO 294-4 |
| Flow : 24 hr | 0.76 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break | 55.2 | MPa | ASTM D638 |
| Break | 55.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 9.9 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.8 | MPa | ASTM D790 |
| -- | 79.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.23 | ||
| vs. Itself - Static | 0.13 | ||
| Wear Factor - Washer | 24.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 1 | 6.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 890 | J/m | ASTM D4812 |
| 23°C 2 | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 178 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 3 | 179 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 170 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 169 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 to 338 | °C | |
| Middle Temperature | 338 to 349 | °C | |
| Front Temperature | 349 to 360 | °C | |
| Processing (Melt) Temp | 360 to 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 AR 10 TFE 20 | RTP Company | Acetal (POM) Copolymer | RTP |
| Riteflex® 677 | Celanese Corporation | TPC-ET | Riteflex® |
| Andur 7501 DP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Forprene® 6NE901A70 | SO.F.TER. SPA | TPV | Forprene® |
| POLYFORT® FPP 1606U | A. Schulman Inc. | PP, Unspecified | POLYFORT® |