CP PRYME® Polystyrene PS100HI-3M
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ELTY86_CPPRYMEPolystyrenePS100HI3M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 3 Melt, Prime High Impact Polystyrene, Natural, FDA Compliant |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 2.6 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 8.5 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 50 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (3.00 mm) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.00 mm) | 55 | % | ASTM D638 |
| Flexural Modulus (5.99 mm) | 1860 | MPa | ASTM D790 |
| Flexural Strength (5.99 mm) | 35.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.00 mm | 150 | J/m | ASTM D256 |
| 23°C, 5.99 mm | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, not annealed | 80.0 | °C | ASTM D648 |
| 1.8 MPa, annealed | 93.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 3 Temp. | 200 - 220 | °C | |
| Cylinder Zone 5 Temp. | 200 - 230 | °C | |
| Die Temperature | 200 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 132495 B | RTP Company | PP, Unspecified | RTP |
| TYNE® Olefins W5223 | Tyne Plastics LLC. | PP, Unspecified | TYNE® Olefins |
| CYCOLOY™ CY5120 resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| Kaneka MUH W2015 | Kaneka Corporation | ABS | Kaneka MUH |
| LUVOCOM® 1850/CF/10/GF/10/BK | LEHVOSS Group | PBT | LUVOCOM® |