EcoPaXX® Q150E
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ELGYvM_EcoPaXX-Q150E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q150E is a Polyamide 410 (Nylon 410) material. It is available in Asia Pacific, Europe, or North America for extrusion or film extrusion. Important attributes of EcoPaXX® Q150E are:
Typical application of EcoPaXX® Q150E: Film |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 5.8 | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | % | |
| Viscosity Number | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.5 | % | |
| Break | 10 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.5 | kJ/m² | |
| 23°C | 5.2 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 250 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content - Carbon | 70 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 466 LV A/B | Wacker Chemie AG | Silicone | POWERSIL® |
| Telcar® TL-87-L832-B | Teknor Apex Company | TPE | Telcar® |
| Moplen RP344N | PolyMirae | PP Random Copolymer | Moplen |
| Lucent PP PPC-310 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| Pro-fax 6331NW | LyondellBasell Industries | PP Homopolymer | Pro-fax |