CALIBRE™ 5201-8
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EKogYO_CALIBRE-5201-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIBRE 5201-8 resin is typically used in electrical market applications. CALIBRE 5201-8 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.36 | g/cm³ | ASTM D792, ISO 1183/B |
| -- | 1330 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Melt volume-flow rate (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 5170 | MPa | ASTM D638 |
| -- | 5170 | MPa | ISO 527-2/50 |
| -- | 5000 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield 5 | 82.7 | MPa | ASTM D638 |
| Yield | 83.0 | MPa | ISO 527-2/50 |
| Yield | 60.0 | MPa | ISO 527-2 6 |
| Break 7 | 82.7 | MPa | ASTM D638 |
| Break | 83.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 8 | 2.6 | % | ASTM D638 |
| Yield | 2.6 | % | ISO 527-2/50 |
| Yield | 2.0 | % | ISO 527-2 9 |
| Break 10 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/50 |
| Nominal strain at break | 30 | % | ISO 527-2 11 |
| Flexural Modulus | |||
| -- 12 | 4830 | MPa | ASTM D790 |
| -- 13 | 4820 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 14 | 148 | MPa | ASTM D790 |
| -- 15 | 148 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 16 | ||
| -30°C | 10.0 | kJ/m² | |
| 23°C | 12.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 17 | ||
| -30°C | 70.0 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Instrumented Dart Impact 18(23°C, Total Energy) | 46.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 148 | °C | ASTM D648, ISO 75-2/B |
| 0.45 MPa | 151 | °C | ISO 75-2 19 |
| 1.8 MPa, Unannealed | 138 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 142 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa | 147 | °C | ISO 75-2 20 |
| Vicat Softening Temperature | |||
| -- | 159 | °C | ASTM D1525 21 |
| -- | 158 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 155 | °C | ISO 306 22 |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ISO 11359-2 23 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 24 | UL 94 | ||
| 1.59 mm | V-2 | ||
| 3.05 mm | V-0 | ||
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | V-2 | ISO 1210 25 | |
| Burning Behav. at thickness h (3.20 mm, UL) | V-2 | ISO 1210 26 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 50 mm/min |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 50 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | 50 mm/min |
| 8 . | 50 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 50 mm/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Method I (3 point load), 2.0 mm/min |
| 13 . | 2.0 mm/min |
| 14 . | Method I (3 point load), 2.0 mm/min |
| 15 . | 2.0 mm/min |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | 3.39 m/sec |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Rate A (50°C/h), Loading 2 (50 N) |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 24 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 25 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 26 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene HFR8294 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Niche PPHG20BK | Niche Polymer, LLC | PP Homopolymer | Niche |
| Hyundai EP PA66 LD150 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| PSM® HL-104 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |
| Sylvin 5150-90 White 1324 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |