Generic Nylon 66 - Glass\Carbon Fiber
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EKUyQt_Generic-Nylon-66---Glass-Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass\Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 - 1.70 | g/cm³ | ASTM D792 |
| 23°C | 1.32 - 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 0.51 | % | ASTM D955 |
| 23°C | 0.24 - 0.46 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12300 - 14000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 184 - 201 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.0 - 3.0 | % | ISO 527-2 |
| Fracture, 23°C | 1.3 - 5.5 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 7400 - 17600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 261 - 293 | MPa | ISO 178 |
| Coefficient of Friction | 0.28 - 0.32 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.9 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 - 65 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 235 - 250 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 245 - 250 | °C | ISO 75-2/A |
| Continuous Use Temperature | 120 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 1.0E+3 - 1.3E+8 | ohms | ASTM D257 |
| -- | 1.0E+2 - 2.5E+10 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 105 | °C | |
| Drying Time | 3.0 - 11 | hr | |
| Rear Temperature | 299 - 300 | °C | |
| Middle Temperature | 287 - 300 | °C | |
| Front Temperature | 299 - 300 | °C | |
| Nozzle Temperature | 290 | °C | |
| Processing (Melt) Temp | 290 - 298 | °C | |
| Mold Temperature | 89.4 - 105 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Glass\Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 GB 20 FR | RTP Company | PC | RTP |
| Restramid PA 6.6 30GF | Polimarky Spolka Jawna | Nylon 66 | Restramid |
| Nanjing Hongrui PA66 A303 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Bapolene® 222B | Bamberger Polymers, Inc. | LDPE | Bapolene® |
| Karina RED PVC COMPOUND -E 780-42/179-A-IS (C800) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |