Durethan® BTC 65 H3.0 EF 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EK25Vq_DurethanBTC65H30EF901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 65% mineral, injection molding, improved heat conductivity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 2.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.68 | % | ISO 294-4 |
| Vertical flow direction : 120°C, 2 hours, 2.00mm 2 | 0.18 | % | ISO 294-4 |
| Flow direction : 280°C, 2.00mm 3 | 0.66 | % | ISO 294-4 |
| Flow direction : 120°C, 2 hours, 2.00mm 4 | 0.16 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 10600 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 160 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA6, GHR, 10-090, MD65 | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 8 | 221 | °C | ISO 11357-3 |
| Thermal Conductivity 9 | 1.0 | W/m/K | ISO 22007-4 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2; MT 80°C; 600 Bar |
| 2 . | 60x60x2 |
| 3 . | 60x60x2; MT 80°C; 600 Bar |
| 4 . | 60x60x2 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| 9 . | Through-Plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR PE CONC 1 NAT | PolyOne Corporation | LDPE | Maxxam™ FR |
| Shinkolite L | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | Shinkolite |
| X-Pro SP 200 TF 13 3325 | CTC Plastics, LLC | PP Copolymer | X-Pro |
| Nylfor® A2 GF/30 FR2/3A NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| LNP™ LUBRICOMP™ Lexan_WR5210R compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |