Shinko-Lac® ASA S710
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EIp6Lo_Shinko-Lac-ASA-S710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Shinko-Lac® ASA S710 is an Acrylonitrile Styrene Acrylate (ASA) material. It is available in North America for injection molding. Primary attribute of Shinko-Lac® ASA S710: Impact Resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/5.0 kg) | 0.70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 31.4 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 1570 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 46.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm, Injection Molded | 95.0 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm, Injection Molded | 77.0 | °C | |
| Vicat Softening Temperature | 87.0 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 FR NH | RTP Company | Nylon 66 | RTP |
| TAIRIPRO K1035 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Witcom PES 6G/3L1 | Witcom Engineering Plastics B.V. | PESU | Witcom PES |
| BR® 57 | Cytec Industries Inc. | PI, TS | BR® |
| LGS 5Z 500 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGS |