Zenite® 7130
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Zenite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EIkNVE_Zenite-7130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Zenite® 7130 is a 30% glass fiber reinforced and lubricated liquid crystal polymer for injection molding. It has excellent impact resistance and excellent heat deflection temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.60 | % | ISO 294-4 |
| Flow direction | 0.010 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 13000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 22 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 310 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 120 | °C | ISO 11357-2 |
| Melting Temperature 2 | 352 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 45 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.10 | IEC 60250 | |
| 1 MHz | 3.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.014 | IEC 60250 | |
| 1 MHz | 0.030 | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | UL 94 | |
| Oxygen Index | 45 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 355 - 365 | °C | |
| Middle Temperature | 360 - 370 | °C | |
| Front Temperature | 360 - 370 | °C | |
| Nozzle Temperature | 360 - 370 | °C | |
| Processing (Melt) Temp | 360 - 370 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 40 to 60°CZone 4 Temperature: 360 to 370°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LH30 | Mando Advanced Materials Co., Ltd. | PP Homopolymer | SEPAZ™ |
| Sylvin 9222-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TES J-50/20/FR | Techmer Engineered Solutions | PC | TES |
| Geon™ Vinyl Flexible R312AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ALTECH® PC ECO 1000/578 | ALBIS PLASTIC GmbH | PC | ALTECH® PC |