Infino HN-1064IA
| Category: | PC , Polycarbonate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EI1KCE_Infino-HN-1064IA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HN-1064IA is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 17 | g/10 min | ASTM D1238 |
| 250°C/10.0 kg | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.50 to 0.62 | % | |
| Across Flow : 3.20 mm | 0.53 to 0.65 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 117 | ASTM D785 | |
| R-Scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2000 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 3 | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 94 | % | ASTM D638 |
| Flexural Modulus | |||
| -- 5 | 1700 | MPa | ASTM D790 |
| -- 6 | 1700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 77.0 | MPa | ASTM D790 |
| -- 8 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 65 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 740 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 640 | J/m | ASTM D256 |
| 23°C 10 | 65 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 127 | °C | ASTM D648 |
| Vicat Softening Temperature | 143 | °C | ISO 306/B50 |
| RTI Elec 11(1.50 mm) | 130 | °C | UL 746 |
| RTI Imp 12(1.50 mm) | 130 | °C | UL 746 |
| RTI Str 13(1.50 mm) | 130 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 240 to 250 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| 11 . | V-0 |
| 12 . | V-0 |
| 13 . | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ELASTOSIL® R plus 573/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® R plus |
| Lucene™ LC165 | LG Chem Ltd. | TPO (POE) | Lucene™ |
| PERCOM® KCT20 | A. Schulman Europe | PP Copolymer | PERCOM® |
| Sylvin 9077A-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL™ NH5020 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |