SCHULAMID® 6 MV 14 FR 4 K1681 DEEP BLACK 96.8086
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EHgqhL_SCHULAMID-6-MV-14-FR-4-K1681-DEEP-BLACK-96-8086.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity flame-retardant Polyamide 6 grade (V-2); without PBDE |
| General Information | |
|---|---|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183/A |
| Viscosity Number | 133 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 62.6 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.3 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.8 | kJ/m² | |
| 23°C | 5.3 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 54 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 180 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 214 | °C | ISO 306/A50 |
| -- | 195 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.400 mm | V-2 | ||
| 0.800 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.380 mm | 960 | °C | |
| 0.750 mm | 930 | °C | |
| 1.50 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.380 mm | 930 | °C | |
| 0.750 mm | 930 | °C | |
| 1.50 mm | 825 | °C | |
| 3.00 mm | 825 | °C | |
| Oxygen Index | 21 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | < 240 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 140 | MPa | |
| Injection Rate | Moderate |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ SAN 2011 G | TER HELL PLASTIC GMBH | SAN | TEREZ SAN |
| Nanjing Hongrui PP P304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Honeywell PCTFE P8000LS | Honeywell | PCTFE | Honeywell PCTFE |
| Karina WHITE PVC COMPOUND -E TR-556D10/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| REV Materials 8008-003 | REV Materials | PP, Unspecified | REV Materials |