Sarlink® TPV X10075B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EGs0kT_Sarlink-TPV-X10075B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink 10000 Series are designed for low friction molding applications, requiring a low coefficient of friction against glass or painted steel. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 5 sec, Extruded | 73 | ||
| Shore A, 5 sec, Injection Molded | 75 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.40 to 0.50 | ASTM D1894 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Across Flow : 100% Strain | 2.80 | MPa | |
| Flow : 100% Strain | 3.50 | MPa | |
| Tensile Stress | ISO 37 | ||
| Across Flow : Break | 6.10 | MPa | |
| Flow : Break | 6.10 | MPa | |
| Tensile Elongation | ISO 37 | ||
| Across Flow : Break | 490 | % | |
| Flow : Break | 410 | % | |
| Tear Strength - Across Flow | 30 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 24 | % | |
| 70°C, 22 hr | 34 | % | |
| 125°C, 70 hr | 50 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ISO 188 | ||
| 135°C, 1000 hr | -15 | % | |
| 100% Strain 135°C, 1000 hr | 5.0 | % | |
| 150°C, 168 hr | -25 | % | |
| 100% Strain 150°C, 168 hr | 0.0 | % | |
| Change in Tensile Strain at Break in Air - Across Flow | ISO 188 | ||
| 135°C, 1000 hr | -20 | % | |
| 150°C, 168 hr | -25 | % | |
| Change in Shore Hardness in Air | ISO 188 | ||
| Shore A, 135°C, 1000 hr | 0.0 | ||
| Shore A, 150°C, 168 hr | -3.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 70 | % | ISO 1817 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 190 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 205 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 180 to 205 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Processing (Melt) Temp | 185 to 210 | °C | |
| Mold Temperature | 10.0 to 55.0 | °C | |
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 100 to 200 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra HoPP 20 Adds | ResMart | PP Homopolymer | ResMart Ultra |
| Shandong PA6 A1R01 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| LNP™ THERMOCOMP™ DX06408 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| Plenco 02000 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| ESTOPLAST ZK 6220NN01 | Ester Industries Ltd. | PC | ESTOPLAST ZK |