Ecdel™ 9965
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Ecdel™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EGgASX_Ecdel-9965.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ecdel™ elastomers are medical grade copolyester ethers (COPE). They offer the clarity, toughness, and chemical resistance needed in a variety of flexible packaging including medical applications. Ecdel™ Elastomer 9965 may be injection molded or extruded. Ecdel™ elastomers may be extrusion blow molded directly into bags or extruded into film for later fabrication into bags. This product has been CRADLE TO CRADLE CERTIFIED Silver. The CRADLE TO CRADLE CERTIFIED Mark is a registered certification mark used under license through McDonough Braungart Design Chemistry (MBDC). MBDC is a global sustainability consulting and product certification firm. The CRADLE TO CRADLE® framework moves beyond the traditional goal of reducing the negative impacts of commerce ('eco-efficiency'), to a new paradigm of increasing its positive impacts ('eco-effectiveness'). At its core, Cradle to Cradle design perceives the safe and productive processes of nature's 'biological metabolism' as a model for developing a 'technical metabolism' flow of industrial materials. Product components can be designed for continuous recovery and reutilization as biological and technical nutrients within these metabolisms. For more information about MBDC and to obtain printable certificates for Eastman Copolyesters, visit www.mbdc.com. Choose Eastman Chemical Company under Company Name in C2C Certified products to display a list of our products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.35 | % | ASTM D570 |
| Inherent Viscosity 1(23°C) | 1.1 | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat of Fusion (23°C) | 27.0 | kJ/kg | ASTM E793 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength (23°C) | 370 | N | ASTM D1004 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 23°C | 95 | ||
| Shore D, 23°C | 55 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 170 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C, 3.00 mm, Injection Molded 2 | 14.0 | MPa | |
| Break, 23°C, 2.00 mm 3 | 20.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 30 | % | |
| Break, 23°C | 300 | % | |
| Flexural Modulus (23°C) | 150 | MPa | ASTM D790 |
| Coefficient of Friction | > 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 130 | µm | |
| Secant Modulus | ASTM D882 | ||
| Tangent, MD : 130 µm | 185 | MPa | |
| Tangent, TD : 130 µm | 179 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 130 µm | 13.7 | MPa | |
| TD : Yield, 130 µm | 13.5 | MPa | |
| MD : Break, 130 µm | 23.7 | MPa | |
| TD : Break, 130 µm | 22.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 130 µm | 26 | % | |
| TD : Yield, 130 µm | 26 | % | |
| MD : Break, 130 µm | 550 | % | |
| TD : Break, 130 µm | 550 | % | |
| Oxygen Permeability (30°C, 130 µm) | 841 | cm³/m²/24 hr | ASTM D1434 |
| Water Vapor Transmission Rate (38°C, 100% RH, 130 µm) | 130 | g/m²/24 hr | ASTM F372 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Clash-Berg Modulus | ASTM D1043 | ||
| -70°C | 930 | MPa | |
| -28°C | 240 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-40°C) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Glass Transition Temperature | -3.00 | °C | DSC |
| Vicat Softening Temperature | 170 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 207 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 140 | °C | DSC |
| CLTE - Flow (23°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | DSC | ||
| 25°C 5 | 1600 | J/kg/°C | |
| 100°C 6 | 1800 | J/kg/°C | |
| 150°C 7 | 2000 | J/kg/°C | |
| 175°C 8 | 2300 | J/kg/°C | |
| 200°C 9 | 3100 | J/kg/°C | |
| 225°C 10 | 2300 | J/kg/°C | |
| Thermal Conductivity (23°C) | 0.19 | W/m/K | ASTM C177 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 130 µm) | 80 | ASTM D2457 | |
| Transmittance | ASTM D1003 | ||
| Total, 130 µm | 93.0 | % | |
| Regular, 130 µm | 90.0 | % | |
| Haze (130 µm) | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | EMN-A-AC-G-V-1 |
| 2 . | Type I, 500 mm/min |
| 3 . | Type IV, 500 mm/min |
| 4 . | Loading 1 (10 N) |
| 5 . | Solid |
| 6 . | Solid |
| 7 . | Solid |
| 8 . | Solid |
| 9 . | Transition, apparent specific heat, including the effects of the heat of fusion. |
| 10 . | Melt |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® ANTISTATIC 60 | API SpA | SEBS | megol® |
| Crastin® ST820 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Daelim Po1y® PP-173 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| Dryflex® 4090 | ELASTO | TPE | Dryflex® |
| Polimid A 25 GF V0F | Poliblend S.p.a. | Nylon 66 | Polimid A |