LNP™ THERMOCOMP™ Noryl_HM3020 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EGfhiB_LNP-THERMOCOMP-Noryl-HM3020-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP NORYL_HM3020 compound is a 30% Glass/Mineral filled, high modulus grade. DTUL 248F (120C). UL94 V-1/5VA rated in black and gray. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.25 | % | |
| Across Flow : 3.20 mm | 0.30 | % | |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 88 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 108 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 7580 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 145 | MPa | ASTM D790 |
| Poisson's Ratio | 0.38 | ASTM D638 | |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Static | 0.42 | ||
| vs. Steel - Static | 0.40 | ||
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 35.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 120 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 95°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -40 to 95°C | 3.4E-5 | cm/cm/°C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm, in Air) | 25 | kV/mm | ASTM D149 |
| Arc Resistance 5 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | ||
| 2.59 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Nozzle Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sypex M1220GN | Ginar Technology Co., LTD. | ABS | Sypex |
| YUNGSOX® PP 1600D | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| NORYL™ PN275 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Geon™ Vinyl Flexible B5D02 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Monprene® CP-38138 XRD4 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |