Plenco 05118 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EGYA6R_Plenco-05118-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 05118 is a mineral and graphite filled phenolic molding compound, formulated for bearing seals. 05118 provides for a low coefficient of friction, abrasion resistance, minimal water absorption, and excellent dimensional stability under severe exposure. 05118 is available in gray. 05118 is not recommended for electrical insulating applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.81 | g/cm³ | ASTM D792 |
| Apparent Density | 0.87 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.17 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 59 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12900 | MPa | ASTM D638 |
| Tensile Strength | 42.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.60 | % | ASTM D638 |
| Flexural Modulus | 11100 | MPa | ASTM D790 |
| Flexural Strength | 69.1 | MPa | ASTM D790 |
| Compressive Strength | 144 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 19.3 | J/m | ASTM D256 |
| Notched Izod Impact | 17 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 192 | °C | ASTM D648 |
| Continuous Use Temperature | 203 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.2E+11 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 18.6 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.051 | ASTM D150 | |
| Comparative Tracking Index (CTI) | 300 | V | UL 746 |
| Additional Information |
|---|
| The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.04%Drop Ball Impact, PLENCO Method: 63 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9456-82 White 1521 | Sylvin Technologies Incorporated | PVC Alloy | Sylvin |
| Xuchuan XCS-2120A | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Karina BLACK PVC COMPOUND 853-48/ 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PEARLSTICK® 45-60/08 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |
| Kepital® FV-30A | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |