Borstar® FB2310
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borstar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EFr4oi_Borstar-FB2310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Borstar FB2310 is a high molecular weight linear low density polyethylene film grade combining good and flexible extrusion behaviour, excellent draw down and superior mechanical properties. For films made of Borstar FB2310 , the high toughness remains in cold conditions. Borstar FB2310 contains antioxidant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.931 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.20 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 20 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 40 µm, blown film | 300 | MPa | ISO 527-3 |
| TD : 40 µm, blown film | 400 | MPa | ISO 527-3 |
| Tensile Strength | ISO 527-3 | ||
| MD : 40 µm, blown film | 50.0 | MPa | ISO 527-3 |
| TD : 40 µm, blown film | 40.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 400 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 700 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 230 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40.0 µm 1 | 50.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm 2 | 250.0 | kN/m | ISO 6383-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumental throwing impact- Total Penetration Energy (40.0 µm) 3 | 200 | J/cm | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 127 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm, Blown Film) | 7 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 80 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| BUR: 3:1FLH: 2 to 4 DDDie Gap: 1 to 1.5 mm |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Fim |
| 3 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP482V | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| Weifang Kingdom CPET101 | Weifang Kingdom Plastic Co., Ltd | CPE | Weifang Kingdom |
| Network Polymers LLDPE 11 2024 | Network Polymers, Inc. | LLDPE | Network Polymers LLDPE |
| Axiall PVC 8652 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Lustran® SMA 2316 | INEOS ABS (USA) | SMA | Lustran® ABS |