Lucalen A2700M

Category:	LDPE , Low Density Polyethylene
Manufacturer:	LyondellBasell Industries
Trademark:	Lucalen
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	EFd3dv_Lucalen-A2700M.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Lucalen A2700M is a low density polyethylene, containing butyl acrylate comonomer.
It exhibits low stiffness, low hardness and good impact properties at low temperature.
Lucalen A2700M is suitable for industrial applications where a combination of good processability and excellent softness is required.
It is compatible with other Lucalen grades and is miscible with other ethylene copolymers, PE-LD, PE-HD and PE-LLD.
The grade is available in natural pellet form.

This grade is not intended for use in medical or pharmaceutical applications

General Information
Features	Durable Good Adhesion Good Chemical Resistance Good Colorability Good Flexibility Good Processability High ESCR (Stress Crack Resist.) High Impact Resistance Low Hardness Low Temperature Flexibility Low Temperature Impact Resistance Opticals Soft Weldable
Uses	Cast Film Film Geo Membranes Industrial Applications Plastics Modification Profiles Sheet Wire & Cable Applications
Appearance	Natural Color
Forms	Pellets
Processing Method	Blown Film Cast Film Compression Molding Extrusion Injection Molding Pipe Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.924	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.2	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance	> 1600	hr	ASTM D1693

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	30		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break, Compression Molded)	11.0	MPa	ISO 527-2/5A
Tensile Strain (Break, Compression Molded)	> 800	%	ISO 527-2/5A
Flexural Modulus	42.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength (-40°C)	No Break		ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	60.0	°C	ISO 306/A50
Melting Temperature	95.0	°C	DSC

Extrusion	Nominal Value	Unit
Melt Temperature	160 to 180	°C

Resin Grade	Manufacturer	Category	Trademark
Tenac™ 7054	Asahi Kasei Chemicals Corporation	Acetal (POM) Homopolymer	Tenac™
Unipren® Elastomers A3 CRLA010 35A EG06IN4 UP332	Petropol Industry and Trade of Polymers LTDA	TPE	Unipren® Elastomers
NEFTEKHIM PP 1554N (F79S)	Nizhnekamskneftekhim Inc.	PP Homopolymer	NEFTEKHIM PP
BLUESTAR® 1130	Nantong Xingchen Synthetic Material Co., Ltd.	PBT	BLUESTAR®
Elexar® EL-3954-55	Teknor Apex Company	TPE	Elexar®