Nypol® PA A3 G30 HS UV PRTA011 NR395
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EEaz3d_Nypol-PA-A3-G30-HS-UV-PRTA011-NR395.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nypol® PA A3 G30 HS UV PRTA011 NR395 is a Polyamide 66 (Nylon 66) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Nypol® PA A3 G30 HS UV PRTA011 NR395 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.37 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.70 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.90 | -- | % | |
| Saturation | 6.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 205 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.3 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 12900 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | -- | 9.0 | kJ/m² | |
| 23°C | 11 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 77 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | -- | 9.0 | kJ/m² | |
| 23°C | 11 | -- | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 110 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 255 | -- | °C | ISO 3146 |
| CLTE | ASTM E831 | |||
| Flow : -40 to 23°C | 2.4E-5 | -- | cm/cm/°C | |
| Flow : 23 to 55°C | 1.8E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.3E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.5E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.3E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.4E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ASTM D257 | |||
| -40°C | -- | 1.0E+13 | ohms·cm | |
| 23°C | 1.0E+14 | -- | ohms·cm |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P1165 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| POLYPRO® 5014L HPT-1 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| TABOND 2006 | SILON s.ro | TPE | TABOND |
| Monprene® MP-1452C | Teknor Apex Company | TPE | Monprene® |
| Sylvin 9812-95 Yellow 405 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |