Generic Nylon 66 - Unspecified
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EEVGBu_Generic-Nylon-66---Unspecified.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Unspecified This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 - 1.92 | g/cm³ | ASTM D792 |
| 23°C | 1.33 - 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (23°C) | 0.19 - 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.35 - 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture, 23°C | 53.8 - 221 | MPa | ASTM D638 |
| Fracture, 23°C | 35.0 - 130 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.0 - 6.9 | % | ASTM D638 |
| Fracture, 23°C | 0.90 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3600 - 11100 | MPa | ASTM D790 |
| 23°C | 3300 - 14000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 82.7 - 134 | MPa | ASTM D790 |
| 23°C | 50.0 - 280 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 - 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 6.0 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 32 - 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 198 - 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 - 250 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 228 - 232 | °C | ISO 75-2/A |
| Melting Temperature | 255 - 260 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.7 - 82.3 | °C | |
| Drying Time | 3.0 - 11 | hr | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 83.3 - 110 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - UnspecifiedThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 603 | RTP Company | ABS | RTP |
| VINIKA® CB55EB | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Nylene® 615 C | Custom Resins Group | Nylon 6 | Nylene® |
| Karina BLACK PVC COMPOUND TR-601D48/1-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plenco 07202 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |