Trexprene® A45NI
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EDoxul_Trexprene-A45NI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Product Description: TREXPRENE ® A45NI is a heat & UV stabilized PP/EPDM based Thermoplastic Vulcanized Elastomer (TPV). This Natural compound is primarily intended for interior applications and can be processed using extrusion, injection, blow molding or other melt processing techniques. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 to 0.980 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 15 sec) | 41 to 47 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wear Resistance 1 | No appreciable loss of grain, texture or color | ASTM D3844 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Properties - Stress at 100% Elongation in Air, 1000 hrs (135°C) | -12 to 12 | % | ISO 188 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Fastness - to Light 2 | Delta E < 3.0 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 3(100% Strain) | 1.30 | MPa | ISO 37 |
| Tensile Stress - Across Flow 4(Yield) | 3.20 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 5(Break) | 430 | % | ISO 37 |
| Tear Strength - Across Flow 6 | 19 | kN/m | ISO 34-1 |
| Compression Set | |||
| 70°C, 22 hr | 30 | % | ASTM D395B |
| 125°C, 70 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr 7 | 30 | % | ISO 815 |
| 125°C, 70 hr 8 | 20 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 1000 hr) | -20 to 10 | % | ISO 188 |
| Change in Tensile Strain at Break in Air (135°C, 1000 hr) | -25 to 10 | % | ISO 188 |
| Change in Shore Hardness in Air (Shore A, 135°C, 1000 hr) | -3.0 to 3.0 | ISO 188 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | |||
| -- | -56.0 | °C | ASTM D746 |
| Type B | -56.0 | °C | ISO 812 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 15 | mm/min | ISO 3795 |
| Note Message | |
|---|---|
| 1 . | 100 cycles, CS10 Wheel, 500 g load |
| 2 . | SAE J2412, 1240.8 kJ/m² |
| 3 . | Type 1, 500 mm/min |
| 4 . | Type 1, 500 mm/min |
| 5 . | Type 1, 500 mm/min |
| 6 . | Method Ba, Angle (Unnicked), 500 mm/min |
| 7 . | Type A |
| 8 . | Type A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® C3 200 TF HS | PolyPacific Pty. Ltd. | PP Copolymer | Retpol® |
| TECOLITE KM-13B(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| NuSil MED1-4161 | NuSil Technology | Silicone | NuSil |
| BLUESTAR® 1084 | Nantong Xingchen Synthetic Material Co., Ltd. | PBT | BLUESTAR® |
| Infino UF-1017S | SAMSUNG SDI CO., LTD. | PC | Infino |