PRL PS-GP1
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EDm2Rz_PRL-PS-GP1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PS-GP1 is a High Impact Polystyrene product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 0.50 to 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 27.6 | MPa | |
| Break, 3.18 mm | 20.7 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.18 mm | 2.0 | % | |
| Break, 3.18 mm | 30 | % | |
| Flexural Modulus (3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 160 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 16.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 76.7 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 71.1 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 188 to 210 | °C | |
| Middle Temperature | 204 to 227 | °C | |
| Front Temperature | 216 to 238 | °C | |
| Processing (Melt) Temp | 218 to 260 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAPPO™ JF303 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Sylvin 5187-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VITAMIDE® AR3XBK8510 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| K-Prene SHEATHING EPR 5064 | Technovinyl Polymers India Ltd. | MPR | K-Prene |
| Sylvin 8280-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |