SUPRAN® LFT PP 2315
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SAMBARK |
| Trademark: | SUPRAN® LFT PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EDbesx_SUPRAN-LFT-PP-2315.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% long glass fiber reinforced light weight purpose Polypropylene. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D648 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 78.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.6 | % | ASTM D638 |
| Flexural Modulus | 3620 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 190 | J/m | |
| 23°C | 180 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 155 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 210 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 C AR 35 | RTP Company | PPS | RTP |
| Sunny® PBT EB230-039 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| TARFLON™ GZK3200 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Amilan® CM3006G-30 | Toray Resin Company | Nylon 66 | Amilan® |
| Bolv ABS | Shandong Jining Bolv Chemicals Co.,Ltd | ABS | Bolv |