Starex VE-1897
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ECl504_StarexVE1897.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Starex VE-1897 is a high impact polystyrene product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.30 - 0.40 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 - 0.50 | % | ASTM D955 |
| Traffic : 3.20mm | 0.30 - 0.40 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 100 | ASTM D785 | |
| R scale | 98 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2060 | MPa | ASTM D638 |
| -- | 2090 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 22.6 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 25.5 | MPa | ASTM D638 |
| Fracture | 22.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 35 | % | ASTM D638 |
| Fracture | 35 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1910 | MPa | ASTM D790 |
| -- 6 | 1600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 31.4 | MPa | ASTM D790 |
| -- 8 | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 93 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 62 | J/m | ASTM D256 |
| 23°C 10 | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, unannealed, 4.00mm | 81.0 | °C | ISO 75-2/B |
| 0.45 MPa, annealing, 4.00mm | 84.0 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 70.0 | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 4.00mm | 79.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 81.0 | °C | ISO 306/B50 |
| -- | 85.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 60 | °C | |
| Hot air dryer | 60 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Mold Temperature | 60 - 80 | °C | |
| Injection Pressure | 68.6 - 206 | MPa | |
| Back Pressure | 0.981 | MPa | |
| Screw Speed | 40 | rpm |
| Injection instructions |
|---|
| Hot Runner Manifold Temperature: 210°CHot Runner Valve Nozzle Temperature: 210°C |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 20 mm/min |
| 4 . | 20 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veromor® Purge -XS | PlastxWorld Inc. | Proprietary | Veromor® Purge |
| AKROMID® B3 GF 30 1 L black (4365) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| LUBEMID A26 EL80 NATURAL | LUBEN PLAST srl | Nylon 66 | LUBEMID |
| OnForce™ LFT NN-30LGF/000 HS SP UV BLACK | PolyOne Corporation | Nylon 66 | OnForce™ LFT |
| StarFlex® 7092-1003 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarFlex® |