Petrothene® NA426225
| Category: | LDPE+EVA , Low Density Polyethylene + EVA |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ECFgc0_Petrothene-NA426225.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA426 is a series of LDPE/EVA copolymer resins selected by customers for high impact and clarity packaging film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 2.5 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 2.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM E111 | ||
| 1% secant, MD | 138 | MPa | ASTM E111 |
| 1% secant, TD | 172 | MPa | ASTM E111 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 22.8 | MPa | ASTM D882 |
| TD : Fracture | 16.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 350 | % | ASTM D882 |
| TD : Fracture | 550 | % | ASTM D882 |
| Dart Drop Impact 1 | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 220 | g | ASTM D1922 |
| TD | 250 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 73 | ASTM D2457 | |
| Haze | 4.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 1.7 - 3.0:1 | ||
| Data obtained from film produced in a 3½" (89 mm) blown film line, commercially available 8" (203 mm) die, 375°F (191°C) melt extrusion temperature, 2:1 BUR, 1.25 mil (32 micron) gauge, 0.025" die gap at 130 lb/hr. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 166 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2102N0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TAROMID A 280 G3 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| VECTRA® MT4310 | Celanese Corporation | LCP | VECTRA® |
| Iupilon® FPR3000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| JSR EPR EP96 | JSR Corporation | EPDM | JSR EPR |