Diamond AES 052
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Diamond AES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EBtZNq_Diamond-AES-052.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Diamond AES 052 is an Acrylonitrile Ethylene Styrene (AES) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(220°C/10.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C, 3.18 mm, Injection Molded) | 0.60 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, 23°C, 3.18 mm, Injection Molded) | 35.3 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3(23°C, 3.18 mm, Injection Molded) | 2140 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, 3.18 mm, Injection Molded) | 58.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm, Injection Molded) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 5 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 232 to 265 | °C | |
| Front Temperature | 235 to 272 | °C | |
| Nozzle Temperature | 220 to 272 | °C | |
| Processing (Melt) Temp | 220 to 272 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 MT 25 FR | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Silopren® LSR 2050 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Bergamid™ XP6042701 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| CONTINUUM™ DGDA-2502 BK | The Dow Chemical Company | HDPE | CONTINUUM™ |
| LNP™ COLORCOMP™ M1000 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ COLORCOMP™ |