MAGNUM™ 8391 MED
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EBXpcf_MAGNUM-8391-MED.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM™ 8391 MED ABS combines an excellent glossy appearance with high flow and medium impact performance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base color that is ideal for self-coloring. MAGNUM 8391 MED natural resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792, ISO 1183/B |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 28 | g/10 min | ASTM D1238, ISO 1133 |
| 230°C/3.8 kg | 8.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (220°C/10.0 kg) | 27.0 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded | 2340 | MPa | ISO 527-2 |
| -- | 2400 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield 4 | 48.0 | MPa | ASTM D638 |
| Yield, 3.20 mm, Injection Molded | 45.0 | MPa | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 47.0 | MPa | ISO 527-2/100 |
| Yield | 48.0 | MPa | ISO 527-2 5 |
| Break 6 | 35.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 7 | 2.7 | % | ASTM D638 |
| Yield, 3.20 mm, Injection Molded | 2.5 | % | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 2.6 | % | ISO 527-2/100 |
| Break 8 | 8.7 | % | ASTM D638 |
| Nominal strain at break | 20 | % | ISO 527-2 9 |
| Flexural Modulus | |||
| -- 10 | 2480 | MPa | ASTM D790 |
| 3.20 mm, Injection Molded | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 11 | 75.0 | MPa | ASTM D790 |
| 3.20 mm, Injection Molded | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 19 | kJ/m² | ISO 179/1eA |
| -30°C | 9.00 | kJ/m² | ISO 179/1eA 12 |
| 23°C | 18.0 | kJ/m² | ISO 179/1eA 13 |
| Charpy impact strength | ISO 179/1eU 14 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 230 | J/m | ASTM D256 |
| -30°C, Injection Molded | 9.0 | kJ/m² | ISO 180/A |
| 23°C, Injection Molded | 19 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 74.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 95.0 | °C | ISO 75-2/A |
| 1.8 MPa | 95.0 | °C | ISO 75-2 15 |
| Vicat Softening Temperature | |||
| -- | 99.0 | °C | ASTM D1525 16 |
| -- | 95.0 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 92.0 | °C | ISO 306 17 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 18(2.00 mm) | 60 | mm/min | ISO 3795 |
| Flame Rating 19 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 20 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | 50 mm/min |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | 50 mm/min |
| 7 . | 50 mm/min |
| 8 . | 50 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 1.3 mm/min |
| 11 . | 1.3 mm/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Rate B (120°C/h), Loading 1 (10 N) |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 19 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E190 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Akulon® Diablo HT-HG0 (K-X07029) | DSM Engineering Plastics | Nylon 66/6 | Akulon® |
| Hifax Premium TKC 176P | LyondellBasell Industries | PP Copolymer | Hifax |
| Huafon HF-1380A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Grilamid® L XE 10987 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |