MAGNUM™ 3904
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EBVHNg_MAGNUM-3904.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM* 3904 is a resin with super-high impact. It is used in a wide range of technical applications. It can be processed by injection moulding, extrusion or thermoforming. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183/B |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.5 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | |||
| 220°C/10.0 kg | 4.70 | cm³/10min | ISO 1133 |
| 220°C/10.0 kg | 4.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded | 1820 | MPa | ISO 527-2 |
| -- | 1900 | MPa | ISO 527-2 3 |
| Tensile Stress | |||
| Yield, 3.20 mm, Injection Molded | 37.0 | MPa | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 39.0 | MPa | ISO 527-2/100 |
| Yield | 35.0 | MPa | ISO 527-2 4 |
| Tensile Strain | |||
| Yield, 3.20 mm, Injection Molded | 2.6 | % | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 2.8 | % | ISO 527-2/100 |
| Yield | 2.5 | % | ISO 527-2 5 |
| Nominal strain at break | 45 | % | ISO 527-2 6 |
| Flexural Modulus (3.20 mm, Injection Molded) | 1900 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 58.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 12 | kJ/m² | ISO 179/2C |
| -30°C, Injection Molded | 18 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 37 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 22 | kJ/m² | ISO 179/2C |
| -30°C | 16.0 | kJ/m² | ISO 179/1eA 7 |
| 23°C | 38.0 | kJ/m² | ISO 179/1eA 8 |
| Charpy impact strength | ISO 179/1eU 9 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 17 | kJ/m² | |
| 23°C, Injection Molded | 42 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Annealed | 97.0 | °C | ISO 75-2/A |
| 1.8 MPa | 97.0 | °C | ISO 75-2 10 |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 97.0 | °C | ISO 306 11 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 12 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 13(2.00 mm) | 40 | mm/min | ISO 3795 |
| Flame Rating 14 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 15 | |
| Carbon Emission 16 | 20.0 | µg/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 14 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCUDIA® EVA PA-441-S | REPSOL | EVA | ALCUDIA® EVA |
| Kingfa PBT R0N | Kingfa | PBT | Kingfa PBT |
| Kumho ASA XC180 | Korea Kumho Petrochemical Co., Ltd. | ASA | Kumho ASA |
| Kuraray K-Polymer SD-1000 | Kuraray Co., Ltd. | PVOH | Kuraray K-Polymer |
| Hostacom ERC 161N C11323 | LyondellBasell Industries | PP Copolymer | Hostacom |