Keripol RW 1411
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Hexion Inc. |
| Trademark: | Keripol |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EAOY6G_Keripol-RW-1411.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Polyester moulding compound, inorganically filled, glass fibre reinforced, styrene free, tracking resistance 600 V, good heat resistance, high viscosity flow characteristics Application Areas H4 lampholders |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 2.10 | g/cm³ | ISO 1183 |
| Apparent Density | 1.00 | g/cm³ | ISO 60 |
| Molding Shrinkage 1 | 0.10 | % | ISO 2577 |
| Water Absorption - 24h/23C | 15.0 | mg | ISO 62 |
| Post Shrinkage 2 | -0.030 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 10.0 | MPa | |
| Compression Molding Temperature | 160 to 180 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 16500 | MPa | ISO 178 |
| Flexural Stress 3 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 160 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength 4(1.00 mm) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 6.00 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 8.0E-3 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 70.0 | °C | |
| Nozzle Temperature | 70.0 to 100 | °C | |
| Processing (Melt) Temp | 70.0 to 100 | °C | |
| Mold Temperature | 160 to 180 | °C | |
| Injection Pressure | > 10.0 | MPa | |
| Back Pressure | 0.500 to 1.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Compression |
| 2 . | Compression |
| 3 . | 2.0 mm/min |
| 4 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 7833-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Xuchuan 2000/B-8580 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| BUPLEN® 6531 | LUKOIL Bulgaria Ltd. | PP Homopolymer | BUPLEN® |
| Geon™ Vinyl Wire & Cable WC9000L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| PLANAC BT-1030-02 | TOYOBO America, Inc. | PBT | PLANAC |