VAMPSON B 3010
| Category: | PPS+PBT , Polyphenylene Sulfide + PBT |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPSON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EA5Vlu_VAMPSON-B-3010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPS/PBT, 30% mixed glass fiber reinforced , halogen and red phosphorus free, high chemical resistance and excellent operating temperature, good mechanicals properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.4 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 5.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | °C | ASTM D648A |
| Vicat Softening Temperature | 245 | °C | ASTM D1525 1 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 | °C | |
| Mold Temperature | 120 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex A0520FN | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Manner Flexible PVC V861 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TOTAL Polypropylene PPC 9760 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Vandar® 8000 | Celanese Corporation | PBT | Vandar® |
| NILAMID® A3 H CF40 | Nilit Plastics | Nylon 66 | NILAMID® |