GLAMIDE® T-663G15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E9MVio_GLAMIDE-T-663G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE®T-663G15 is a polyamide 66 (nylon 66) product, which contains a 15% glass fiber reinforced material. It is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.26 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 10 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.70 - 1.0 | -- | % | ASTM D955 |
| 3.00 mm | 0.80 - 1.1 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.0 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 2.1 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 160 | 145 | MPa | ASTM D638 |
| Yield, 23°C | 120 | 90.0 | MPa | ASTM D638 |
| Yield, 80°C | 60.0 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.5 | 7.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 6200 | 5900 | MPa | ASTM D790 |
| 23°C | 5400 | 3500 | MPa | ASTM D790 |
| 80°C | 2500 | 2100 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 200 | 170 | MPa | ASTM D790 |
| Yield, 23°C | 160 | 120 | MPa | ASTM D790 |
| Yield, 80°C | 100 | 75.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 50 | 55 | J/m | ASTM D256 |
| 23°C | 70 | 110 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 262 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 245 | -- | °C | ASTM D648 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.00 | -- | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.010 | -- | ASTM D150 | |
| Arc Resistance | 110 | 90.0 | sec | ASTM D495 |
| Comparative Tracking Index | 575 | 575 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 调节后的 Volume Resistivity, ASTM D257: 1e10 to 1e11 ohm-m |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 66 Prime Series PG15-01BL | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Eco-Solutions GP9001T | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| Kelon® B FR H2 CEG/500-V0CT3 | LATI S.p.A. | Nylon 6 | Kelon® B |
| Karina IVORY PVC COMPOUND 90540-35/1-Y-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1-8130 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |