Envir® PA6G33VL-BK0801
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Barnet |
| Trademark: | Envir® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E95eIB_Envir-PA6G33VL-BK0801.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Envir® PA6G33VL-BK0801 is a 33% Glass fiber reinforced Nylon 6 molding resin. It is a Value added "upcycled" compound with a good balance of properties. 6G33VL incorporates a high recycled material content, giving it a truly "green" appeal. It is provided Black in color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Ash Content | 33 | % | ASTM D5630 |
| Moisture Content | < 0.20 | % | ASTM D6980 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Granularity | 3.50 | g/100 pellets |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2 |
| Flexural Modulus | 9650 | MPa | ISO 178 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 38 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTOLIT® P 1352 K | VESTOLIT GmbH & Co. KG | PVC Homopolymer | VESTOLIT® |
| FHR Polypropylene P9M7R-056 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| FRAGOM PR/900 | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| KOPA® KN3322V0BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Infino NE-1030 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |