MEGOLON™ S530
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | AlphaGary |
| Trademark: | MEGOLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E8sitI_MEGOLON-S530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MEGOLON™ S530 is a thermoplastic, halogen free, fire retardant sheathing compound possessing very good flexibility and a low Young's Modulus. It has been specifically developed for telecommunication cable applications and exhibits a high oxygen index and enhanced fire test performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 1.5 | g/10 min | ISO 1133 |
| Mooney Viscosity (ML 1+4, 140°C) | 50 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| -- 1 | 14.5 | MPa | IEC 60811-1-2 |
| -- | 11.5 | MPa | IEC 60811-1-1 |
| Tensile Strain | |||
| Break 2 | 130 | % | IEC 60811-1-2 |
| Break | 180 | % | IEC 60811-1-1 |
| Elongation at Break | |||
| after 4 hours, in IRM 902 Oil : 70°C | 170 | % | |
| after 4 hours, in SAE 20 Oil : 70°C | 210 | % | |
| after 7 days, in IRM 902 Oil : 23°C | 140 | % | |
| after 7 days, in IRM 903 Oil : 23°C | 170 | % | |
| Tensile Strength | |||
| after 4 hours, in IRM 902 Oil : 70°C | 11.0 | MPa | |
| after 4 hours, in SAE 20 Oil : 70°C | 8.60 | MPa | |
| after 7 days, in IRM 902 Oil : 23°C | 11.5 | MPa | |
| after 7 days, in IRM 903 Oil : 23°C | 5.20 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold Elongation (-25°C) | 40 | % | IEC 60811-1-4 |
| Cold Impact (-25°C) | pass | IEC 60811-1-4 | |
| Hot Deformation (90°C) | 5.0 | % | BS 6469 99.1 |
| Hot Pressure Test (80°C) | 33 | % | IEC 60811-3-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | BS 6469 99.2 | ||
| 20°C | 6.0E+13 | ohms·cm | |
| after 12 hours immersion in water : 20°C | 1.0E+13 | ohms·cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Acid Gas Emission Conductivity | 42.0 | µS/cm | IEC 60754-2 |
| Acid Gas Emission pH | 4.50 | IEC 60754-2 | |
| Flammability Temperature Index | 300 | °C | ISO 4589-3 |
| Smoke Density | ASTM E662 | ||
| Flaming mode 3 | < 48 | Ds | |
| Non-flaming mode 4 | < 350 | Ds | |
| Toxicity | 1.60 | NES 713 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | 0.0 | % | IEC 60754-1 |
| Ozone Resistance | pass | ASTM D470 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Draw Down | 1.5:1.0 | ||
| Extruder Screw Compression Ratio | 1.0:1.0 to 2.0:1.0 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 5.00 | kN/m | BS 6469 99.1 |
| Aging | Nominal Value | Unit | |
|---|---|---|---|
| Change in Tensile Strength in Air (100°C, 168 hr) | 26 | % | |
| Change in Tensile Strain at Break in Air (100°C, 168 hr) | -28 | % | |
| Change in Tensile Stress | |||
| 23°C, 168 hr, in IRM 902 Oil | 0.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | -55 | % | |
| 70°C, 4 hr, in IRM 902 Oil | -5.0 | % | |
| 70°C, 4 hr, in SAE 20 Oil | -25 | % | |
| Change in Tensile Strain at Break | |||
| 23°C, 168 hr, in IRM 902 Oil | -22 | % | |
| 23°C, 168 hr, in IRM 903 Oil | -5.0 | % | |
| 70°C, 4 hr, in IRM 902 Oil | -5.0 | % | |
| 70°C, 4 hr, in SAE 20 Oil | 15 | % | |
| Change in Volume | |||
| 23°C, 168 hr, in IRM 902 Oil | 0.0 | % | |
| 23°C, 168 hr, in IRM 903 Oil | 16 | % | |
| 70°C, 4 hr, in IRM 902 Oil | 1.0 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (50 Hz) | 3.80 | ASTM D150 | |
| Dissipation Factor (50 Hz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 40 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 140 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 150 | °C | |
| Cylinder Zone 5 Temp. | 160 | °C | |
| Melt Temperature | 165 to 175 | °C | |
| Die Temperature | 165 | °C |
| Note Message | |
|---|---|
| 1 . | after 7 days at 100°C |
| 2 . | after 7 days at 100°C |
| 3 . | Time to maximum: 11 minutes |
| 4 . | Time to maximum: 12 minutes |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GF 30 FRG 5 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| TAROMID B 280 G8 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Nanguang TPU Y-80AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| Karina IVORY PVC COMPOUND -E CAK 65 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kepamid® 2300SF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |