MAJORIS ET432 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E8TmBn_MAJORIS-ET432---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ET432 - 8229 is a mineral filled polypropylene compound intended for injection moulding. The product is available in black (ET432 - 8229) and natural (ET432) but other colours can be provided on request. ET432 - 8229 has a very easy flowing and excellent mechanical properties. ET432 - 8229 has been developed especially for the automotive under the bonnet applications requiring long-term heat stability. ET432 - 8229 makes it very easy to process for complicated part with long flow paths. APPLICATIONS
Products requiring good long-term heat resistance, very high heat distortion temperature, excellent rigidity, high dimensional stability, low shrinkage can suitably be made from ET432 - 8229. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 - 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture | 30 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 134 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 82.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A |
| -- | 103 | °C | ISO 306/B |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Stability (150°C) | > 700.0 | hr |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASTALAC™ ASA 304 | Marplex Australia Pty. Ltd. | ASA | ASTALAC™ |
| Ethylplus 619 LD | Fainplast Compounds S.r.l | LDPE | Ethylplus |
| ECONAMID® 6ST2 | DOMO Engineering Plastics SPA | Nylon 6 | ECONAMID® |
| Hostacom PPU X9067HS G62514 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 8369-90FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |