Kinta NB2630G
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E8NZ9L_KintaNB2630G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta NB2630G is a polypropylene product that contains a 30% glass fiber reinforced material. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 85.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 9.0 | % | ASTM D638 |
| Flexural Modulus 3 | 5000 | MPa | ASTM D790 |
| Flexural Strength 4 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 8.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 150 | °C | ASTM D648 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 41 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 80 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 200 - 205 | °C | |
| Middle Temperature | 200 - 215 | °C | |
| Front Temperature | 200 - 205 | °C | |
| Nozzle Temperature | 205 - 210 | °C | |
| Processing (Melt) Temp | 198 - 210 | °C | |
| Mold Temperature | 90 - 100 | °C | |
| Injection Pressure | 100 - 130 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Asrene® SF 5008E | Chandra Asri Petrochemical | HDPE | Asrene® |
| KEP® 240 | Kumho Polychem Co., Ltd. | EPDM | KEP® |
| Karina STRAW COLOR CONCENTRATE 38/ 49-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GRAY PVC COMPOUND -E 828-18/569-Y-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SIBUR Synthetic Rubber NBR 1865 | SIBUR | NBR | SIBUR Synthetic Rubber |