Makropol® PC B3 LF FD CRLA010 PC321
| Category: | PC , Polycarbonate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Makropol® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E75hGc_Makropol-PC-B3-LF-FD-CRLA010-PC321.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate transparent,high viscosity, FDA - food contact quality, good hydrolysis resistance. Indicated for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Across Flow | 0.75 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| Saturation, 23°C | 0.30 | % | |
| Equilibrium | 0.12 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 111 | MPa | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2350 | MPa | ASTM D638 |
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 130 | % | ASTM D638 |
| Flexural Modulus 2 | 2350 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 18 | kJ/m² | |
| 23°C | 80 | kJ/m² | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -30°C | 16.0 | kJ/m² | |
| 23°C | 90.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 141 | °C | |
| 1.8 MPa, Unannealed | 129 | °C | |
| Vicat Softening Temperature | 150 | °C | ASTM D1525 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Electric Strength | 34 | kV/mm | IEC 60243-1 |
| Dissipation Factor (1 MHz) | 9.5E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 930 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 265 to 290 | °C | |
| Mold Temperature | 70.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY PA917G4 | Polyram Ram-On Industries | Nylon 66+PP | RAMLLOY |
| TECHNYL® B 216 NATURAL D | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® B |
| Colorite Rigid PVC 1118G-WHITE 532 | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Desmopan® DP 9873DU | Covestro - PUR | TPU-Polyether | Desmopan® |
| Lucky Enpla LAY100F | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |