CYCOLOY™ CM6240 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | E6ZNE6_CYCOLOY-CM6240-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CYCOLOY CM6240 resin is a flame retardant PC/ABS blend featuring balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems intended to meet thin wall flame resistance and various environmental requirements. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 17 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.33 | % | |
| Flow : 3.20 mm | 0.30 to 0.40 | % | |
| Across Flow | 0.38 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.10 | % | |
| Equilibrium, 23°C, 50% RH | 0.030 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4350 | MPa | ASTM D638 |
| -- | 4460 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/5 |
| Break 3 | 40.0 | MPa | ASTM D638 |
| Break | 29.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Break 5 | 35 | % | ASTM D638 |
| Break | 25 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4400 | MPa | ASTM D790 |
| -- 7 | 4510 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 101 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 23°C | 86 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 7.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 35.0 | J | |
| 23°C, Total Energy | 56.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 86.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ASTM D1525, ISO 306/B50 11 13 |
| -- | 100 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm, Testing by SABIC | V-0 | ||
| 1.50 mm, Testing by SABIC | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 16 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 220 to 255 | °C | |
| Middle Temperature | 230 to 275 | °C | |
| Front Temperature | 255 to 285 | °C | |
| Nozzle Temperature | 255 to 285 | °C | |
| Processing (Melt) Temp | 255 to 285 | °C | |
| Mold Temperature | 70.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 U | NUREL, S.A. | Nylon 6 | Promyde® |
| Quantum Composites QC-2430 | Quantum Composites Inc. | Phenolic | Quantum Composites |
| McCann PP M30CHPP10 | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| Network Polymers PP PPB 25 2010 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| EVALENE® PP PRB0201 | JG Summit Petrochemical Corporation | PP Random Copolymer | EVALENE® PP |